Click for Home Click for Profile Brass Parts Fittings manufacturers, exporters of competitive brass plumbing, cable glands, hose fittings, electrical components, screws and brass fittings Brass Parts Fittings brass plumbing fittings electrical components electrical accessories brass hardware Hose Fittings Brass Wood Screws Brass Pipe Fittings Brass Nuts Brass Components Brass Fittings Brass Turned Parts India manufacturers Brass Nuts Brass Fasteners copper lugs hose barbs SS fittings hose connectors Brass inserts sanitary fittings Click for Email Click for Resources Click for Feedback Click for Downloads
Click for Manufacturing site
Click for Export World
Click for Contact us
Click for Site Map
Click for FAQ
Click for Packaging Information
 

Copper Alloy No. C93700

High Leaded Tin Bronze SAE 64 , CDA 937 , 80-10-10

ASTM B 505 , ASTM B 271

Chemical Composition % by weight

 

Element Nominal Minimum Maximum
Aluminum - - .005
Antimony - - .55
Copper 80 78 82
Iron - - .15
Lead 10 8 11
Nickel - - 1
Phosphorus - - .15
Silicon - - .005
Sulfur - - .08
Tin 10 9 11
Zinc - - .8

 

C93700 has excellent machining properties, medium strength and good corrosion resistance and will withstand mild acids as found in mine water.

Bearings manufactured from C93700 have excellent wear resistance under conditions of high speed, heavy pressure and vibration, have low friction and can be used where lubrication is less than adequate and there may be minor misalignment. C93700 bearings require a hardened shaft and maximum shaft surface speeds of 4 m/sec can be tolerated.

 

Applications

 

Bearings for high speed and heavy pressures, pumps, impellers, corrosion resistant applications, pressure tight castings. 

Mechanical Properties

M07 - As Continuous Cast

Hardness* Brinell Hardness (500 kg load) 60
Tensile Strength** KSI 35
Yield Strength ** KSI (0.5% Ext. under load) 20
Elongation** % in 2 inch 20

**Test values are nominal approximations and depend on specimen size and orientation.

Physical Properties

Thermal Conductivity BTU/ (sq ft-ft-hr-F) 27.1
Specific Heat BTU/lb/F @ 68F .09
Thermal Expansion Per F from 68 F to 392 F .0000103
Density lb/cu in @ 68 F .320
Electrical Conductivity* (Annealed) % IACS @ 68 F 10
Modulus of Elasticity KSI 11,000

*Volume basis

Fabrication Practices

Stress relieving temperature 500 F or 260 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment No
Machinability rating (Free Cutting Brass=100) 80
Suitability for being joined by: Soldering/Good
  Brazing/Good*
  Oxyacetylene Welding/Not Recommended
  Gas Shielded Arc Welding/Not Recommended
  Coated Metal Arc Welding/Not Recommended

*Since brazing is performed at temperatures within the hot-short range, strain must be avoided during the brazing and cooling of this alloy.

The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.