Click for Home Click for Profile Brass Parts Fittings manufacturers, exporters of competitive brass plumbing, cable glands, hose fittings, electrical components, screws and brass fittings Brass Parts Fittings brass plumbing fittings electrical components electrical accessories brass hardware Hose Fittings Brass Wood Screws Brass Pipe Fittings Brass Nuts Brass Components Brass Fittings Brass Turned Parts India manufacturers Brass Nuts Brass Fasteners copper lugs hose barbs SS fittings hose connectors Brass inserts sanitary fittings Click for Email Click for Resources Click for Feedback Click for Downloads
Click for Manufacturing site
Click for Export World
Click for Contact us
Click for Site Map
Click for FAQ
Click for Packaging Information
 

Copper Alloy No. C95400

Aluminum Bronze 9C ,  , CDA 954 , Grade C

ASTM B 505 , ASTM B 271

Chemical Composition % by weight

 

Element Nominal Minimum Maximum
Aluminum 11 10 11.5
Copper 85 83 -
Iron 4 3 5
Manganese - - .50
Nickel - - 2.5

 

Application for Castings

Bearings, gears, worm gears, bushings, wear plate, valve seats and guides, pickling hooks. 

 

Mechanical Properties (as cast)

 

M07 - As Continuous Cast

Hardness* Brinell Hardness (3000 kg load) 170
Tensile Strength** KSI 85 min
Yield Strength ** KSI (0.5% Ext. under load) 32 min
Elongation** % in 2 inch 10 min

**Test values are nominal approximations and depend on specimen size and orientation.

Physical Properties

Thermal Conductivity BTU/ (sq ft-ft-hr-F) 33.9
Specific Heat BTU/lb/F @ 68F .10
Thermal Expansion Per F from 68 F to 572 F .000009
Density lb/cu in @ 68 F .269
Electrical Conductivity* (Annealed) % IACS @ 68 F 13
Modulus of Elasticity KSI 15,500

*Volume basis

Fabrication Practices

Stress relieving temperature 600 F or 316 C
Time at temperature 1 hour per inch of section thickness
Responds to heat treatment Yes
Solution heat treating temperature 1600-1675 F or 870-910 C
Time at temperature 1 hour per inch of section thickness
Quenching medium Water
Annealing temperature 1150-1225 F or 620-660 C
Time at temperature 1 hour per inch of section thickness
Machinability rating (Free Cutting Brass=100) 60
Suitability for being joined by: Soldering/Good
  Brazing/Good
  Oxyacetylene Welding/Not Recommended
  Carbon Arc Welding/Fair
  Gas Shielded Arc Welding/Very Good
  Coated Metal Arc Welding/Good

The values listed above represent reasonable approximations suitable for general engineering use. Due to commercial variations in composition and to manufacturing limitations, they should not be used for specification purposes. See applicable A.S.T.M. specification references.